Test your basic knowledge |

Engineering Materials

Subject : engineering
Instructions:
  • Answer 50 questions in 15 minutes.
  • If you are not ready to take this test, you can study here.
  • Match each statement with the correct term.
  • Don't refresh. All questions and answers are randomly picked and ordered every time you load a test.

This is a study tool. The 3 wrong answers for each question are randomly chosen from answers to other questions. So, you might find at times the answers obvious, but you will see it re-enforces your understanding as you take the test each time.
1. 1. Imperfections increase resistivity - grain boundaries - dislocations - impurity atoms - vacancies 2. Resistivity - increases with temperature - wt% impurity - and %CW






2. 1. Tc= critical temperature- if T>Tc not superconducting 2. Jc= critical current density - if J>Jc not superconducting 3. Hc= critical magnetic field - if H > Hc not superconducting






3. 1. Ability of the material to absorb energy prior to fracture 2. Short term dynamic stressing - Car collisions - Bullets - Athletic equipment 3. This is different than toughness; energy necessary to push a crack (flaw) through a material 4. Useful in






4. - The emission of light from a substance due to the absorption of energy. (Could be radiation - mechanical - or chemical energy. Could also be energetic particles.) - Traps and activator levels are produced by impurity additions to the material - Whe






5. The magnetic hysteresis phenomenon: Stage 1: Initial (unmagnetized state) Stage 2: Apply H - align domains Stage 3: Remove H - alignment remains => Permanent magnet Stage 4: Coercivity - Hc negative H needed to demagnitize Stage 5: Apply -H - align d






6. Rho=F/A - tau=G/A . Depending on what angle the force is applied - and what angle the crystal is at - it takes different amounts of force to induce plastic deformation.






7. Sigma=ln(li/lo)






8. A measure of the ease with which a B field can be induced inside a material.






9. Occur when lots of dislocations move.






10. As the applied field (H) increases the magnetic domains change shape and size by movement of domain boundaries.






11. Liquid polymer at room T - sandwiched between two sheets of glass - coated with transparent - electrically conductive film. - Character forming letters/ numbers etched on the face - Voltage applied disrupts the orientation of the rod- shaped molecule






12. 1. Electron motions 2. The spins on electrons - Net atomic magnetic moment: sum of moments from all electrons.






13. Defines the ability of a material to resist fracture even when a flaw exists - Directly depends on size of flaw and material properties - K(ic) is a materials constant






14. Undergo extensive plastic deformation prior to failure.






15. 1. Yield = ratio of functional chips to total # of chips - Most yield loss during wafer processing - b/c of complex 2. Reliability - No device has infinite lifetime. Statistical methods to predict expected lifetime - Failure mechanisms: Diffusion reg






16. High toughness; material resists crack propagation.






17. There is always some statistical distribution of flaws or defects.






18. Transformer cores require soft magnetic materials - which are easily magnetized and de-magnetized - and have high electrical resistivity - Energy losses in transformers could be minimized if their cores were fabricated such that the easy magnetizatio






19. The Magnetization of the material - and is essentially the dipole moment per unit volume. It is proportional to the applied field. Xm is the magnetic susceptibility.






20. - A magnetic field is induced in the material B= Magnetic Induction (tesla) inside the material mu= permeability of a solid






21. 1. Hard disk drives (granular/perpendicular media) 2. Recording tape (particulate media)






22. 1. Diamagnetic (Xm ~ 10^-5) - small and negative magnetic susceptibilities 2. Paramagnetic (Xm ~ 10^-4) - small and positive magnetic susceptibilities 3. Ferromagnetic - large magnetic susceptibilities 4. Ferrimagnetic (Xm as large as 10^6) - large m






23. Measures impact energy 1. Strike a notched sample with an anvil 2. Measure how far the anvil travels following impact 3. Distance traveled is related to energy required to break the sample 4. Very high rate of loading. Makes materials more "brittle."






24. Process by which geometric patterns are transferred from a mask (reticle) to a surface of a chip to form the device.






25. Growth of an oxide layer by the reaction of oxygen with the substrate - Provides dopant masking and device isolation - IC technology uses 1. Thermal grown oxidation (dry) 2. Wet Oxidation 3. Selective Oxidation






26. 1. General yielding occurs if flaw size a < a(critical) 2. Catastrophic fast fracture occurs if flaw size a > a(critical)






27. This strength parameter is similar in magnitude to a tensile strength. Fracture occurs along the outermost sample edge - which is under a tensile load.






28. Increase temperature - no increase in interatomic separation - no thermal expansion






29. A parallel-plate capacitor involves an insulator - or dielectric - between two metal electrodes. The charge density buildup at the capacitor surface is related to the dielectric constant of the material.






30. 1. Data for Pure Silicon - electrical conductivity increases with T - opposite to metals






31. The ability of a material to be rapidly cooled and not fracture






32. # of thermally generated electrons = # of holes (broken bonds)






33. Is reflected - absorbed - scattered - and/or transmitted: Io=It+Ia+Ir+Is






34. Process by which metal atoms diffuse because of a potential.






35. ...occurs in bcc metals but not in fcc metals.






36. Created by current through a coil N= total number of turns L= length of turns (m) I= current (ampere) H= applied magnetic field (ampere-turns/m) Bo= magnetic flux density in a vacuum (tesla)






37. (sigma)=K(sigma)^n . K = strength coefficient - n = work hardening rate or strain hardening exponent. Large n value increases strength and hardness.






38. Flaws and Defects - They concentrate stress locally to levels high enough to rupture bonds.






39. Not ALL the light is refracted - SOME is reflected. Materials with a high index of refraction also have high reflectance - High R is bad for lens applications - since this leads to undesirable light losses or interference.






40. For a metal - there is no ______ - only reflection






41. Small Coercivities - Used for electric motors - Example: commercial iron 99.95 Fe






42. Measures Hardness 1. psia = 500 x HB 2. MPa = 3.45 x HB






43. Width of smallest feature obtainable on Si surface






44. Reflectiviy is between 0.90 and 0.95 - Metal surfaces appear shiny - Most of absorbed light is reflected at the same wavelength (NO REFRACTION) - Small fraction of light may be absorbed - Color of reflected light depends on wavelength distribution of






45. They are used to assess properties of ceramics & glasses.






46. Light Amplification by Stimulated Emission of Radiation






47. Occur due to: restrained thermal expansion/contraction -temperature gradients that lead to differential dimensional changes sigma = Thermal Stress






48. Wet: isotropic - under cut Dry: ansiotropic - directional






49. 1. Stress-strain behavior is not usually determined via tensile tests 2. Material fails before it yields 3. Bend/flexure tests are often used instead.






50. Elastic means reversible! This is not a permanent deformation.