1. Smaller the deformation - _______ the recrystallization temperature.






2. Heating to recovery temperature relieves internal stresses






3. Greater the degree of deformation - _________ are the recrystallized grains.






4. If metal is held at recrystallization temperature long enough - cold worked structure is completely replaced with recrystallized grain structure.






5. Recrystallization temperature increases with ______ of metals.






6. Dislocations are moved into _______ configuration.






7. Amount of prior deformation - Temperature and time - Initial grain size - Composition of metal.






8. Approximately 0.4 times the absolute melting temperature to induce rapid recovery.






9. Formation of sub- grain structure) takes place.






10. Because the number of dislocation is greatly reduced - the recrystallized metal has _________ but lower strength.






11. Strain energy of cold work is stored as dislocations






12. Higher the temperature - is the time required for recrystallization.






13. Cold worked metals become brittle.






14. For Recrystallization - A minimum amount of _______ is needed.






15. Recrystallization occurs by the nucleation and growth of new grains containing few dislocations.






16. Reheating - which increases ductility results in recovery - recrystallization and grain growth. This is call ______ and changes material properties.






17. Additional thermal energy permits disloctions to move and form boundaries of a polygonized subgrain structure. From a practical point of view - the principal change in the metal during recovery is the reduction of stresses.






18. Expansion of nucleus and migration of grains.