Test your basic knowledge |

Modern Material Science And Engineering 4

Subject : engineering
Instructions:
  • Answer 50 questions in 15 minutes.
  • If you are not ready to take this test, you can study here.
  • Match each statement with the correct term.
  • Don't refresh. All questions and answers are randomly picked and ordered every time you load a test.

This is a study tool. The 3 wrong answers for each question are randomly chosen from answers to other questions. So, you might find at times the answers obvious, but you will see it re-enforces your understanding as you take the test each time.
1. The application of stresses parallel to a crack causing the top portion to be pushed forward and the bottom portion to be pulled in the opposite direction






2. The number of cycles at a given stress level that a material can experience before failing






3. The first stage of creep - during which dislocations in a material slip and move around obstacles






4. Method used to determine fatigue by alternating compressive and tensile forces on the sample






5. A method used to determine the tensile strength - breaking strength - and the yield strength of a sample






6. Failure because of repeated stresses bellow the yield strength






7. The region on a stress - strain curve in which no permanent changes to the material occur






8. Materials that fail completely at the onset of plastic deformation. these materials have linear stress - strain curves






9. The application of stress perpendicular to a crack - wich pulls the top and bottom potions in opposite directions






10. The amount of flexural stress a material can withstand before breaking. measured through the bend test






11. A specific method of measuring the resistance of a materials surface to penetration by a hard object under a static force






12. The amount of energy lost as the test sample is destroyed during an impact test






13. Test that approximate the impact of an environmental variable on a material over time by exposing the material to a higher level of that variable for shorter times






14. A value used to determine if two distinct sets of examples are statistically different






15. The stress at the highest applied force on a stress - strain curve






16. Plastic deformation of a material under stress at elevated temperatures; occurs due to dislocations in the material






17. Relates the longitudinal deformation and the lateral deformation of material under stress


18. The resistance of the surface of a material to penetration by a hard object under static force






19. A statistical table based on the degrees of freedom and the level of uncertainty in a set of reported sample values






20. The transition of some metals in which a change in temperature causes them to transform between ductile and brittle behavior






21. The change in the slope of the strain - time plot at any given point during a creep test






22. A method used to measure the resistance of the surface of a material to penetration by a hard object under a static force






23. The stress at which the material breaks completely during tensile testing






24. The fracture toughness above the critical thickness in which the width of the material no longer impacts the fracture toughness






25. The region on the stress - strain curve in which the material has experienced a change from which it will not completely recover






26. The slope of the stress - strain curve in the elastic region. aka Young's Modulus and Tensile Modulus






27. The degree of certainty in an estimate of a mean






28. A curve plotting the results of testing multiple samples at different stress levels that used to to determine the fatigue life of a material at a given stress level






29. The study of crack growth leading to material failure






30. The stage in which the rate that dislocations propagate equals the rate at which the dislocations are blocked - resulting in a fairly linear region on the strain - time plot






31. A ratio of the force applied to a sample and the instantaneous length of the chain to the initial length of the chain






32. The ratio of applied load to cross - sectional area






33. Term that accounts for the increased stress applied to an elliptical crack whose length is much greater than its width






34. The area contained under the elastic portion of a stress - strain curve - which represent how much energy the material can absorb before permanently beforming






35. A property defining a materials resistance to a blow that is measured by an impact test






36. Stresses that act perpendicularly to the direction of the crack - causing the crack ends to pull apart and opening the crack further






37. The ratio of the elastic energy to the strain at yielding - which determines how much energy will be used for deformation and how much will be translated to motion






38. The stress level below which there is a 50% probability that failure will never occur






39. A limit placed on the accuracy of a reported mean - based on the number of samples tested - the standard deviation - and the desired level of confidence






40. An estimate of the transition between elastic stretching and plastic deformation for a material without a linear region stress - strain curve






41. The sudden decrease in cross - sectional area of a region of a sample under a tensile load






42. The final stage of creep - during which the rate of deformations accelerates rapidly and continues until rupture






43. The ease with which a material deforms without breaking






44. The ratio of the maximum stress to the applied stress






45. Cracks - voids - and other inperfections in a material that cause highly localized increases in stress






46. A method used to measure the flexural strength of a sample






47. A value used to characterized creep based on time - temperature - and material- specific constants






48. The stress at the point of transition between elastic stretching and plastic deformation






49. A property determined by measuring the change in the length of a sample to initial length of the sample






50. A single blow test names after Charpy in which a notched test sample is broken by a swinging pendulum