1. A ratio of the force applied to a sample and the instantaneous length of the chain to the initial length of the chain






2. The final stage of creep - during which the rate of deformations accelerates rapidly and continues until rupture






3. Failure because of repeated stresses bellow the yield strength






4. A property determined by measuring the change in the length of a sample to initial length of the sample






5. Stress values not involving the presence of stress raisers in the material






6. The region on a stress - strain curve in which no permanent changes to the material occur






7. The area contained under the elastic portion of a stress - strain curve - which represent how much energy the material can absorb before permanently beforming






8. Guidelines published by the American Society for Testing and Materials that provide detailed testing procedures to ensure that tests performed in different laboratories are directly comparable






9. The value that the stress concentration factor must exceed to allow a crack to propogate






10. The resistance of the surface of a material to penetration by a hard object under static force






11. Relates the longitudinal deformation and the lateral deformation of material under stress


12. A property defining a materials resistance to a blow that is measured by an impact test






13. A single blow test names after Charpy in which a notched test sample is broken by a swinging pendulum






14. The application of stress perpendicular to a crack - wich pulls the top and bottom potions in opposite directions






15. A value used to determine if two distinct sets of examples are statistically different






16. A method used to determine the tensile strength - breaking strength - and the yield strength of a sample






17. The stress level below which there is a 50% probability that failure will never occur






18. The region on the stress - strain curve in which the material has experienced a change from which it will not completely recover






19. A value used to characterized creep based on time - temperature - and material- specific constants






20. Test that approximate the impact of an environmental variable on a material over time by exposing the material to a higher level of that variable for shorter times






21. The stage in which the rate that dislocations propagate equals the rate at which the dislocations are blocked - resulting in a fairly linear region on the strain - time plot






22. The transition of some metals in which a change in temperature causes them to transform between ductile and brittle behavior






23. Materials that fail completely at the onset of plastic deformation. these materials have linear stress - strain curves






24. A curve plotting the results of testing multiple samples at different stress levels that used to to determine the fatigue life of a material at a given stress level






25. The application of stresses parallel to a crack causing the top portion to be pushed forward and the bottom portion to be pulled in the opposite direction






26. A period used to force the same aging processes to occur on a sample in a shorter amount of time






27. A method used to measure the resistance of the surface of a material to penetration by a hard object under a static force






28. Term that accounts for the increased stress applied to an elliptical crack whose length is much greater than its width






29. The ratio of applied load to cross - sectional area






30. The amount of energy lost as the test sample is destroyed during an impact test






31. The number of cycles at a given stress level that a material can experience before failing






32. A statistical table based on the degrees of freedom and the level of uncertainty in a set of reported sample values






33. The fracture toughness above the critical thickness in which the width of the material no longer impacts the fracture toughness






34. The first stage of creep - during which dislocations in a material slip and move around obstacles






35. The slope of the stress - strain curve in the elastic region. aka Young's Modulus and Tensile Modulus






36. The amount of flexural stress a material can withstand before breaking. measured through the bend test






37. Materials that can plastically deform without breaking






38. The stress at which the material breaks completely during tensile testing






39. An impact test similar to the charpy test in which the sample is aligned vertically with the notch facing away from the hammer






40. Plastic deformation of a material under stress at elevated temperatures; occurs due to dislocations in the material






41. A specific method of measuring the resistance of a materials surface to penetration by a hard object under a static force






42. An estimate of the transition between elastic stretching and plastic deformation for a material without a linear region stress - strain curve






43. The ease with which a material deforms without breaking






44. The ratio of the elastic energy to the strain at yielding - which determines how much energy will be used for deformation and how much will be translated to motion






45. The study of crack growth leading to material failure






46. A limit placed on the accuracy of a reported mean - based on the number of samples tested - the standard deviation - and the desired level of confidence






47. The degree of certainty in an estimate of a mean






48. The change in the slope of the strain - time plot at any given point during a creep test






49. Method used to determine fatigue by alternating compressive and tensile forces on the sample






50. A method used to measure the flexural strength of a sample