1. A value used to determine if two distinct sets of examples are statistically different






2. The study of crack growth leading to material failure






3. A single blow test names after Charpy in which a notched test sample is broken by a swinging pendulum






4. An impact test similar to the charpy test in which the sample is aligned vertically with the notch facing away from the hammer






5. The fracture toughness above the critical thickness in which the width of the material no longer impacts the fracture toughness






6. The square root of the variance. this value provides more knowledge about the distance from the mean a random sample is likely to be






7. Failure because of repeated stresses bellow the yield strength






8. A limit placed on the accuracy of a reported mean - based on the number of samples tested - the standard deviation - and the desired level of confidence






9. The stress at the highest applied force on a stress - strain curve






10. The change in the slope of the strain - time plot at any given point during a creep test






11. Cracks - voids - and other inperfections in a material that cause highly localized increases in stress






12. The resistance of the surface of a material to penetration by a hard object under static force






13. The sudden decrease in cross - sectional area of a region of a sample under a tensile load






14. An estimate of the transition between elastic stretching and plastic deformation for a material without a linear region stress - strain curve






15. Stresses that act perpendicularly to the direction of the crack - causing the crack ends to pull apart and opening the crack further






16. The application of stress perpendicular to a crack - wich pulls the top and bottom potions in opposite directions






17. A property defining a materials resistance to a blow that is measured by an impact test






18. The final stage of creep - during which the rate of deformations accelerates rapidly and continues until rupture






19. One of the many scales used to evaluate the resistance of a materials surface to penetration by a hard object under static force






20. The transition of some metals in which a change in temperature causes them to transform between ductile and brittle behavior






21. Plastic deformation of a material under stress at elevated temperatures; occurs due to dislocations in the material






22. The ease with which a material deforms without breaking






23. Relates the longitudinal deformation and the lateral deformation of material under stress


24. The stage in which the rate that dislocations propagate equals the rate at which the dislocations are blocked - resulting in a fairly linear region on the strain - time plot






25. Method used to determine fatigue by alternating compressive and tensile forces on the sample






26. The stress at which the material breaks completely during tensile testing






27. The value that the stress concentration factor must exceed to allow a crack to propogate






28. The application of stresses parallel to a crack causing the top portion to be pushed forward and the bottom portion to be pulled in the opposite direction






29. The region on a stress - strain curve in which no permanent changes to the material occur






30. The degree of certainty in an estimate of a mean






31. A value used to characterized creep based on time - temperature - and material- specific constants






32. A statistical quantity that takes into account the random error from a variety of sources and provides infromation about the spread of the data






33. Materials that fail completely at the onset of plastic deformation. these materials have linear stress - strain curves






34. A method used to determine the tensile strength - breaking strength - and the yield strength of a sample






35. Materials that can plastically deform without breaking






36. Guidelines published by the American Society for Testing and Materials that provide detailed testing procedures to ensure that tests performed in different laboratories are directly comparable






37. The amount of flexural stress a material can withstand before breaking. measured through the bend test






38. A nonlinear - qualitative scaled used to evaluate the resistance of a materials surface to penetration by a hard object






39. The region on the stress - strain curve in which the material has experienced a change from which it will not completely recover






40. A curve plotting the results of testing multiple samples at different stress levels that used to to determine the fatigue life of a material at a given stress level






41. The ratio of the maximum stress to the applied stress






42. A ratio of the force applied to a sample and the instantaneous length of the chain to the initial length of the chain






43. A statistical table based on the degrees of freedom and the level of uncertainty in a set of reported sample values






44. Term that accounts for the increased stress applied to an elliptical crack whose length is much greater than its width






45. The amount of energy lost as the test sample is destroyed during an impact test






46. A period used to force the same aging processes to occur on a sample in a shorter amount of time






47. The stress level below which there is a 50% probability that failure will never occur






48. The ratio of the elastic energy to the strain at yielding - which determines how much energy will be used for deformation and how much will be translated to motion






49. The stress at the point of transition between elastic stretching and plastic deformation






50. The first stage of creep - during which dislocations in a material slip and move around obstacles